Caracterização tecnológica de uma mistura de sinter feed e pellet feed para uso em processo HPS.
dc.contributor.advisor | Silva, Gilberto Henrique Tavares Álvares da | pt_BR |
dc.contributor.advisor | Vieira, Cláudio Batista | pt_BR |
dc.contributor.author | Lima, Alinne Júlia de Araújo Souza | |
dc.contributor.emailOrientador | gilbertoalvares@ucloud.com | pt_BR |
dc.contributor.emailOrientador | ensinosuperior@icloud.com | pt_BR |
dc.contributor.referee | Silva, Gilberto Henrique Tavares Álvares da | pt_BR |
dc.contributor.referee | Vieira, Cláudio Batista | pt_BR |
dc.contributor.referee | Lemos, Leandro Rocha | pt_BR |
dc.contributor.referee | Bagatini, Maurício Covcevich | pt_BR |
dc.date.accessioned | 2020-11-18T14:17:15Z | |
dc.date.available | 2020-11-18T14:17:15Z | |
dc.date.issued | 2019 | pt_BR |
dc.description | Programa de Pós-Graduação em Engenharia de Materiais. Departamento de Engenharia Metalúrgica, Escola de Minas, Universidade Federal de Ouro Preto. | pt_BR |
dc.description.abstract | O Quadrilátero Ferrífero (QF) encontra-se inserido na porção sudoeste do Cráton São Francisco e apresenta importantes reservas de minério de ferro no estado de Minas Gerais. A relação MH/MI (minérios hematíticos/minérios itabiríticos) no ROM, ao longo das últimas décadas, tem-se mostrado cada vez menor. Ademais, o sinter feed produzido tem se tornado ao longo dos últimos anos cada vez mais fino quando comparado com a situação de décadas passadas. Assim, tem-se observado um considerável aumento das frações -0,15mm e diminuição daquelas +1,0mm no minério. Essa mudança das características granulométricas do sinter feed tem forte impacto negativo na permeabilidade do leito de sinterização, e consequentemente contribui para diminuição da produtividade dos processos convencionais de sinterização. O processo não convencional HPS (Hybrid Pelletized Sinter), de tecnologia japonesa, tem sido utilizado como alternativa para afinamento do sinter feed. No entanto ainda não é conhecido o efeito do afinamento do sinter feed com introdução de concentrados de itabirito na mistura de minérios nesse processo. Nesse contexto, o principal objetivo desse trabalho é fazer uma caracterização tecnológica de misturas de pellet feed, concentrado obtido a partir de concentração magnética de um minério itabirítico, e sinter feed hematítico para uso em processo HPS. Inicialmente, foi feita caracterização do sinter feed hematítico e do pellet feed. Essa caracterização foi feita em termos de granulometria, química, granuloquímica, mineralogia, water holding e análise de propriedades em altas temperaturas (assimilação e penetração de líquidos). Posteriormente, foi realizada a avaliação da eficiência do fenômeno de formação de quase-partículas (micropelotização), de misturas a sinterizar empregando sinter feed e pellet feed em planta piloto HPS por meio da avaliação das medidas dos índices de granulação dessas misturas. Em seguida feita avaliação em planta piloto HPS do desempenho de quatro misturas a sinterizar empregando o sinter feed e o pellet feed em diferentes proporções (sendo a Mistura 1 para apenas sinter feed hematítico, Mistura 2 para 70% sinter feed hematítico e 30% pellet feed concentrado com granulometria mais grosseira, Mistura 3 para 70% sinter feed hematítico e 30% pellet feed concentrado com mesma granulometria da Mistura 1, e, por fim, a Mistura 4 para 60% de sinter feed hematítico e 40% de pellet feed concentrado com afinamento do minério, com elevação em 10% na fração <0,150mm em relação à Mistura 1). Após as queimas na planta piloto, os sínteres produzidos foram caracterizados em termos de análise química, granulométrica, física, metalúrgica e mineralógica. O teor de SiO2 da amostra de pellet feed concentrado se mostrou inferior ao do sinter feed hematítico (4,05% e 5,80%, respectivamente) e, como esperado, a granulometria do primeiro se apresentou consideravelmente mais fina (72% de fração <0,150mm) em relação ao segundo (38% de fração <0,150mm). Sobre a mineralogia, a amostra do pellet feed concentrado apresentou maior quantidade de partículas de hematita lamelar em relação do sinter feed hematítico, além de menor grau de liberação. Pelo teste de water holding foi observado que a fração aderente do sinter feed hematítico possui uma capacidade um pouco maior de absorver água em relação à mesma fração do pellet feed concentrado. Quanto aos resultados dos testes a altas temperaturas (teste de assimilação e penetração de líquidos), conclui-se que o concentrado de itabirito, que possui menor teor de minerais de ganga favorece o processo de aglomeração a quente, aumentando o rendimento de sinterização e a resistência física do sínter, com formação de uma estrutura com poros mais bem distribuídos e esféricos. Pelos testes em planta piloto, foi possível observar que para a Mistura 2, contendo o sinter feed hematítico e o pellet feed, com elevada relação de partículas nucleante/aderente (1,15) não foi identificada perda de produtividade em relação a fase referência, sem pellet feed concentrado (Mistura 1) - pelo contrário, a produtividade se mostrou superior em relação à fase referência. Quando houve participação de pellet feed em 30% na mistura, sem, contudo, haver alteração da curva granulométrica (Mistura 3 em relação à Mistura 1), a produtividade se mostrou no mesmo nível em relação à fase referência indicando que o consumo de concentrado não interfere negativamente na produtividade da sinterização, quando a granulometria do blend de minério não é alterada. Por outro lado, quando ocorreu uma redução na relação de partículas grossas sobre as partículas finas (como foi o caso da Mistura 4 em relação à Mistura 1), a produtividade tendeu a ser reduzida, de modo que a elevação em 10% na fração <0,150mm resultou em perda de produtividade de aproximadamente 8%. Com relação à qualidade dos sínteres pilotos, pelos ensaios metalúrgicos (RI e RDI), o sínter de melhor resultado foi aquele com maior quantidade de concentrado e com menor relação nucleante/aderente (Mistura 4), que apresentou menor velocidade de sinterização e menor teor de contaminantes. | pt_BR |
dc.description.abstracten | The Quadrilátero Ferrífeto (QF) is located in the southwest portion of the São Francisco Craton and has important iron ore reserves in the state of Minas Gerais. The ratio MH / MI (hematitic ore / itabiritic ores) in ROM over the last decades has been decreasing. Moreover, the sinter feed iron ore produced has become increasingly finer over the last few years compared to the situation of past decades. Thus, a considerable increase of -0.15mm fractions and a decrease of + 1.0mm in the ore has been observed. This change in sinter feed particle size characteristics has a strong negative impact on the sintering bed permeability, and consequently contributes to decreased productivity of conventional sintering processes. The unconventional HPS (Hybrid Pelletized Sinter) process, from Japanese technology, has been used as an alternative for sinter feed trend of reducing size distribution, however the effect of finer sinter feed with the introduction of itabirite concentrates into the ore mixture is not yet known in this process. In this context, the main objective of this work is to make a technological characterization of pellet feed mixtures, concentrate obtained from magnetic concentration of an itabirite ore, and hematitic sinter feed for use in HPS process. Initially, hematitic sinter feed and pellet feed were characterized. This characterization was made in terms of granulometry, chemistry, granulochemistry, mineralogy, water holding and properties analysis at high temperatures (liquid assimilation and liquid penetration). Subsequently, the efficiency of the quasi-particle formation (micropellotization) phenomenon of sintering mixtures was evaluated using sinter feed and pellet feed in a HPS pilot plant by evaluating the measurements of the granulation indices of these mixtures. The HPS pilot plant was then used to evaluate the performance of four sinter mixtures using sinter feed and pellet feed in different ratios (Mix 1 for hematitic sinter feed only, Mix 2 for 70% hematitic sinter feed and 30% pellet feed concentrate with coarser grain size, Mix 3 for 70% hematitic sinter feed and 30% pellet feed concentrate with same grain size as Mix 1, and finally Mix 4 for 60% hematitic sinter feed and 40% pellet feed concentrate with ore smaller grain size, with a 10% increase in the fraction <0.150mm compared to Mixture 1). After produced in the pilot plant, the sinter were characterized in terms of chemical, particle size, physical, metallurgical and mineralogical analysis. The SiO2 content of the concentrated pellet feed sample was lower than the hematitic sinter feed (4.05% and 5.80%, respectively) and, as expected, the granulometry of the former was considerably finer (72% fraction <0.150mm) compared to the second (38% fraction <0.150mm). Concerning mineralogy, the concentrated pellet feed sample presented a larger amount of lamellar hematite particles than the hematitic sinter feed, as well as a lower mineral liberation. The water holding test showed that the adherent fraction of the hematitic sinter feed has a slightly higher capacity to absorb water compared to the same fraction of the concentrated pellet feed. Regarding the results of the tests at high temperatures (liquid assimilation and liquid penetration test), it can be concluded that the itabirite concentrate, which has lower contaminant content, favors the hot agglomeration process, increasing the sintering yield and physical resistance of the sinter, forming a structure with better distributed and spherical pores. From the pilot plant tests, it was observed that for Mix 2, containing the hematitic sinter feed and the pellet feed, with a high nucleating / adherent particle ratio (1,15), presented no productivity loss in relation to the reference phase, without concentrated pellet feed (Mix 1) - on the contrary, the productivity was higher than the reference phase. When there was a 30% pellet feed participation in the mixture, without, however, changing the particle size curve (Mix 3 in relation to Mix 1), the productivity was at the same level in relation to the reference phase indicating that the consumption of concentrate does not interfere negatively on the sintering productivity when the grain size of the ore blend is not changed. On the other hand, when there was a reduction in the ratio of coarse particles to fine particles (as it was the case with Mix 4 relative to Mix 1), productivity tended to be reduced, so that the 10% increase in fraction < 0.150mm resulted in a productivity loss of approximately 8%. Regarding the quality of the pilot sinter, by the metallurgical tests (RI and RDI), the sinter with the best result was the one with the highest amount of concentrate and the lowest nucleant / adherent ratio (Mixture 4), which presented lower sintering speed and lower content. of contaminants. | pt_BR |
dc.identifier.citation | LIMA, Alinne Júlia de Araújo Souza. Caracterização tecnológica de uma mistura de sinter feed e pellet feed para uso em processo HPS. 125 f. 2019. Dissertação (Mestrado em Engenharia de Materiais) – Escola de Minas, Universidade Federal de Ouro Preto, Ouro Preto, 2019. | pt_BR |
dc.identifier.uri | http://www.repositorio.ufop.br/handle/123456789/12924 | |
dc.language.iso | pt_BR | pt_BR |
dc.rights | aberto | pt_BR |
dc.rights.license | Autorização concedida ao Repositório Institucional da UFOP pelo(a) autor(a) em 14/10/2019 com as seguintes condições: disponível sob Licença Creative Commons 4.0 que permite copiar, distribuir e transmitir o trabalho, desde que sejam citados o autor e o licenciante. Não permite o uso para fins comerciais nem a adaptação. | pt_BR |
dc.subject | Sinterização | pt_BR |
dc.subject | Beneficiamento de minério | pt_BR |
dc.subject | Flotação | pt_BR |
dc.subject | Granulometria | pt_BR |
dc.title | Caracterização tecnológica de uma mistura de sinter feed e pellet feed para uso em processo HPS. | pt_BR |
dc.type | Dissertacao | pt_BR |
Files
Original bundle
1 - 1 of 1
No Thumbnail Available
- Name:
- DISSERTAÇÃO_CaracterizaçãoTecnológicaMistura.pdf
- Size:
- 20.46 MB
- Format:
- Adobe Portable Document Format
License bundle
1 - 1 of 1
No Thumbnail Available
- Name:
- license.txt
- Size:
- 924 B
- Format:
- Item-specific license agreed upon to submission
- Description: