Efeito do teor de Cromo e Nióbio na resistência ao desgaste abrasivo de revestimentos duros do tipo Fe-C-Cr.
| dc.contributor.advisor | Costa, Adilson Rodrigues da | pt_BR |
| dc.contributor.author | Oliveira, Tatiane Gabi de | |
| dc.contributor.referee | Costa, Adilson Rodrigues da | pt_BR |
| dc.contributor.referee | Caldeira, Lecino | pt_BR |
| dc.contributor.referee | Solé, Rubén Antonio Llobell | pt_BR |
| dc.contributor.referee | Silva, Gilberto Henrique Tavares Álvares da | pt_BR |
| dc.date.accessioned | 2020-07-16T14:23:35Z | |
| dc.date.available | 2020-07-16T14:23:35Z | |
| dc.date.issued | 2019 | |
| dc.description | Programa de Pós-Graduação em Engenharia de Materiais. Departamento de Engenharia Metalúrgica, Escola de Minas, Universidade Federal de Ouro Preto. | pt_BR |
| dc.description.abstract | Neste trabalho é feita uma avaliação da influência do teor de cromo e da combinação do cromo e nióbio em ligas de revestimento duro do tipo Fe-Cr-C, na microestrutura e propriedades que envolvam a resistência ao desgaste microabrasivo. Vários estudos têm sido realizados em busca de informações conclusivas sobre este sistema em condições de desgaste, devido às distintas fases e propriedades apresentadas por estas ligas. As ligas de Fe-Cr-C associam fases duras (carbonetos), com uma matriz metálica, o que lhes proporciona elevada dureza e resistência mecânica. Para realização dos experimentos, foram utilizadas as ligas de Fe-Cr-C comerciais, em forma de consumíveis (eletrodos e arame) e aplicadas em aço carbono ASTM A36 por meio de processos de Soldagem ao Arco Elétrico com Eletrodo Revestido (SMAW) e Soldagem ao Arco Elétrico com Atmosfera de Proteção Gasosa (GMAW), respectivamente, como revestimentos. Neste caso, foram utilizados dois eletrodos com adição de 25 e 45% em peso de cromo e um arame com 20 e 5% em peso de cromo e nióbio, respectivamente. O ensaio de desgaste por microabrasão foi realizado utilizando o teste por esfera rotativa fixa e, como abrasivo, uma suspensão de diamante de granulação 3µm. Para o qual, foram utilizados 4 corpos de prova referentes à cada liga. Para determinar o coeficiente de desgaste foi obtida a perda média de volume de material, em intervalos de tempo de ensaio pré-estabelecidos, relacionando o resultado com a distância de deslizamento. Ao analisar os resultados obtidos, verificou-se que a liga que apresentou combinação de cromo e nióbio em sua composição exibiu melhores resultados de resistência ao desgaste, embora apresentasse menores valores de dureza e percentual de carbonetos em relação às outras duas ligas. O percentual de carbonetos é um fator importante na análise de resistência ao desgaste quando avaliado juntamente com outras características. Tal fato evidencia a possibilidade de se utilizar tais ligas em aplicações que requerem alto desempenho em relação à resistência ao desgaste. | pt_BR |
| dc.description.abstracten | This paper presents an evaluation of the influence of chromium content and the blend of chromium and niobium in Fe-Cr-C hardfacing alloys on the microstructure and properties that involve microabrasive wear resistance. Various studies have been carried out searching for conclusive information on this system under wear conditions, due to the different phases and properties presented by these alloys. These alloys associate carbides with a metallic matrix giving them high hardness and mechanical resistance. For the realization of the experiments, commercial Fe-Cr-C alloys were obtained in the form of consumables (electrodes and wire) and applied as coatings on ASTM A36 carbon steel by means of Shielded Metal Arc Welding (SMAW) and Gas Metal Arc Welding (GMAW) welding processes, respectively. In this case, two electrodes with addition of 25 and 45 percent by weight of chromium and a wire with 20 and 5 percent by weight of chromium and niobium, respectively, were used. The microabrasion wear test was performed using the fixed rotating ball method and, as an abrasive, a diamond suspension of 3μm granulation. For this, four test specimens were used for each alloy. In order to calculate the wear coefficient, the average loss in volume was determined at pre-established time intervals, relating the result to the sliding distance. When analyzing the obtained results, it was verified that the alloy that presented the combination of chromium and niobium in its composition had better wear resistance results, although it showed lower values of hardness and volume fraction of carbide in comparison to the other two alloys. The carbide volume fraction is an important factor in the analysis of wear resistance when evaluated together with the morphological and dimensional characteristics of these particles. Such result evidences the possibility of using such alloy in applications that require high performance in relation to wear resistance. | pt_BR |
| dc.identifier.citation | OLIVEIRA, Tatiane Gabi de. Efeito do teor de Cromo e Nióbio na resistência ao desgaste abrasivo de revestimentos duros do tipo Fe-C-Cr. 2019. 89 f. Dissertação (Mestrado em Engenharia de Materiais) – Escola de Minas, Universidade Federal de Ouro Preto, Ouro Preto, 2019. | pt_BR |
| dc.identifier.uri | http://www.repositorio.ufop.br/handle/123456789/12460 | |
| dc.language.iso | pt_BR | pt_BR |
| dc.rights | aberto | pt_BR |
| dc.rights.license | Autorização concedida ao Repositório Institucional da UFOP pelo(a) autor(a) em 21/05/2019 com as seguintes condições: disponível sob Licença Creative Commons 4.0 que permite copiar, distribuir e transmitir o trabalho desde que sejam citados o autor e o licenciante. Não permite o uso para fins comerciais nem a adaptação. | pt_BR |
| dc.subject | Nióbio | pt_BR |
| dc.subject | Desgaste | pt_BR |
| dc.subject | Abrasão | pt_BR |
| dc.subject | Resistência | pt_BR |
| dc.title | Efeito do teor de Cromo e Nióbio na resistência ao desgaste abrasivo de revestimentos duros do tipo Fe-C-Cr. | pt_BR |
| dc.type | Artigo publicado em periodico | pt_BR |