O uso da metalografia quantitativa para análise das correlações existentes entre as propriedades físicas e mecânicas da matriz metálica 25%Fe-50%Cu-25%NbH obtida por prensagem a quente.

Simple item page
dc.contributor.advisorAssis, Paulo Santospt_BR
dc.contributor.advisorOliveira, Hellen Cristine Prata dept_BR
dc.contributor.authorMartins, Marina Furbino
dc.contributor.refereeAssis, Paulo Santospt_BR
dc.contributor.refereeQueiroz, Rhelman Rossano Urzedopt_BR
dc.contributor.refereeBatista, Adriano Corrêapt_BR
dc.contributor.refereeMurta, Jorge Luiz Bresciapt_BR
dc.contributor.refereeOliveira, Hellen Cristine Prata dept_BR
dc.date.accessioned2021-08-12T00:48:52Z
dc.date.available2021-08-12T00:48:52Z
dc.date.issued2020pt_BR
dc.descriptionPrograma de Pós-Graduação em Engenharia de Materiais. Departamento de Engenharia Metalúrgica, Escola de Minas, Universidade Federal de Ouro Preto.pt_BR
dc.description.abstractPor aliar menor consumo de energia com maior aproveitamento de matéria prima, a metalurgia do pó apresenta grande potencial como processo de fabricação. Para melhor compreensão do comportamento do sinterizado, é fundamental estabelecer correlações entre microestrutura e propriedades. Neste trabalho, avaliou-se a matriz metálica 25%Fe-50%Cu-25%NbH obtida por prensagem a quente sob diferentes temperaturas de sinterização, seguido pela metalografia quantitativa e a busca pelas correlações com suas propriedades físicas e mecânicas. As matrizes foram sinterizadas por 3 min, à pressão de 35 MPa nas temperaturas de 750 °C, 800 °C, 850 °C, 900 °C e 950 °C. As amostras foram submetidas aos ensaios de dureza Vickers e de flexão, à microscopia eletrônica de varredura e à difração de raios X. Foram quantificadas também porosidade, área média de partícula e densidade aparente. A prensagem a quente favoreceu a sinterização por fase sólida para Fe e Nb e por fase líquida para o Cu. Foi possível observar que as propriedades do material estão intimamente relacionadas às temperaturas do processo, suficientes para provocar a desidrogenação do hidreto e proporcionar a formação de novas fases como FeNb, Fe2Nb e Fe7Nb6. O aumento da temperatura de sinterização favoreceu mecanismos de difusão e endurecimento do material, revelando maior dureza (113,32 kgf/mm2 ), módulo de elasticidade (138,12 GPa) e tensão máxima (377,76 MPa) à 950 °C. Para esta temperatura foi identificado a menor área média de partícula de Nb (57,47 µm2 ). Por outro lado, a maior efetividade de sinterização foi observada para as amostras obtidas a 900 °C, quando foram calculados os melhores valores de densidade aparente (7,80 g/cm3 ) e porosidade (0,253%). A diminuição da quantidade de poros na estrutura do material tende a melhorar suas propriedades mecânicas e, por isso, à 900 °C o material apresentou elevados valores de dureza (94,67 kgf/mm2 ), módulo de elasticidade (113,54 GPa) e tensão máxima (364,21 MPa). Para esta temperatura foi identificado a menor área média de partícula de Fe (348,32 µm2 ).pt_BR
dc.description.abstractenFor combining lower energy consumption with greater use of raw material, powder metallurgy has great potential as a manufacturing process. It is essential to establish correlations between microstructure and properties to better understand the behavior of the sample. In this work, the metallic matrix 25%Fe-50%Cu-25%HNb obtained by hot pressing under different sintering temperatures was evaluated, followed by quantitative metallography and the search for correlations with its physical and mechanical properties. The matrices were sintered during 3 minutes, at a pressure of 35 MPa at temperatures of 750 °C, 800 °C, 850 °C, 900 °C and 950 °C. The samples were submitted to Vickers hardness and flexion tests, scanning electron microscopy and X-ray diffraction analysis. Porosity, average particle area and density were also quantified. Hot pressing supported solid-phase sintering for Fe and Nb, and liquid phase sintering for Cu. It was observed that the material properties are closely related to the process temperatures, enough to cause the dehydrogenation and provide the formation of new phases such as FeNb, Fe2Nb and Fe7Nb6. The increase in the sintering temperature favored mechanisms of diffusion and hardening of the material, revealing greater hardness (113,32 kgf/mm2 ), elastic modulus (138,12 GPa) and maximum stress (377,76 MPa) at 950 °C. For this temperature, the smallest average particle area of Nb (57,471 µm2 ) was identified. On the other hand, the highest sintering effectiveness was observed for samples obtained at 900 °C, when the best apparent density (7,80 g/cm3 ) and porosity (0,253%) values were calculated. The decrease in the amount of pores in the material structure tends to improve its mechanical properties and, therefore, at 900 °C the material presented high values of hardness (94,67 kgf/mm2 ), modulus of elasticity (113,54 GPa) and maximum tension (364,21 MPa). For this temperature, the smallest average particle area of Fe (348,32 µm2 ) was identified.pt_BR
dc.identifier.citationMARTINS, Marina Furbino. O uso da metalografia quantitativa para análise das correlações existentes entre as propriedades físicas e mecânicas da matriz metálica 25%Fe-50%Cu-25%NbH obtida por prensagem a quente. 2020. 109 f. Dissertação (Mestrado em Engenharia de Materiais) – Escola de Minas, Universidade Federal de Ouro Preto, Ouro Preto, 2020.pt_BR
dc.identifier.urihttp://www.repositorio.ufop.br/jspui/handle/123456789/13467
dc.language.isopt_BRpt_BR
dc.rightsabertopt_BR
dc.rights.licenseAutorização concedida ao Repositório Institucional da UFOP pelo(a) autor(a) em 0/0/0 com as seguintes condições: disponível sob Licença Creative Commons 4.0 que permite copiar, distribuir e transmitir o trabalho, desde que sejam citados o autor e o licenciante. Não permite o uso para fins comerciais nem a adaptação.pt_BR
dc.rights.urihttp://creativecommons.org/licenses/by-nc-nd/3.0/us/*
dc.subjectMetalurgia do pópt_BR
dc.subjectCompostos de nióbio - hidreto de nióbiopt_BR
dc.subjectMetais - propriedades mecânicaspt_BR
dc.subjectMetalografiapt_BR
dc.subjectLigas - metalurgia - Fe-Cu-NbHpt_BR
dc.titleO uso da metalografia quantitativa para análise das correlações existentes entre as propriedades físicas e mecânicas da matriz metálica 25%Fe-50%Cu-25%NbH obtida por prensagem a quente.pt_BR
dc.typeDissertacaopt_BR
Files
Original bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
DISSERTAÇÃO_UsoMetalografiaQuantitativa.pdf
Size:
5.3 MB
Format:
Adobe Portable Document Format
Description:
Download
License bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
license.txt
Size:
1.71 KB
Format:
Item-specific license agreed upon to submission
Description:
Download
Collections
REDEMAT - Mestrado (Dissertações)