Caracterização da matéria-prima com tamanho de partículas nanométricas utilizadas no processamento do compósito WC-10%Co.

Simple item page
dc.contributor.authorBatista, Adriano Corrêa
dc.contributor.authorAguiar, Amanda Maia
dc.contributor.authorOliveira, Hellen Cristine Prata de
dc.contributor.authorAssis, Paulo Santos
dc.date.accessioned2021-12-21T17:27:21Z
dc.date.available2021-12-21T17:27:21Z
dc.date.issued2020pt_BR
dc.description.abstractO compósito WC-10%Co também conhecido como Metal Duro de Carbeto de Tungstênico (WC) com Cobalto (Co) é um dos materiais mais produzidas pela indústria fabricante de metal duro, entretanto busca-se o melhor entendimento sobre o efeito de parâmetros de processo sobre as suas características estruturais, especialmente no que diz respeito à formação de fases metaestáveis – fases η. Neste trabalho, usamos o método de Rietveld aliado a difração de raios X (DRX), a microscopia eletrônica de varredura (MEV) e o Brunauer – Emmett – Teller (BET) para investigar a estrutura das matérias-primas utilizadas na produção de metal duro. Os tamanhos das partículas assim como as morfologias identificadas para os pós de WC e Co são reflexos do seu processo de fabricação que, introduzem tensões residuais para o pó de WC, a baixa cristalinidade e significante parcela de amorfo para o pó de Co. Estas características foram identificadas com a difração de raios X em comparação com o padrão de difração obtido e os bancos de dados cristalográficos. Após o processo de mistura dos pós foram quantificadas as fases e identificados os efeitos desse processo sobre as células unitárias de cada fase. Este trabalho mostra que a rota de caracterização empregada, com o uso do método de Rietveld, é eficiente para analisar a estrutura desses materiais durante seu processamento. Foi possível observar que o processo de mistura utilizando equipamento de moagem de alta energia promove alteração na densidade das células unitárias do WC “empurrando” átomos de Co para dentro de sua estrutura. Isso pode vir a acelerar o processo de dissolução de grande parte das partículas de WC durante a sinterização, contribuindo para a formação acentuada das fases metaestáveis eta – η, prejudicando o equilíbrio entre as propriedades mecânicas de dureza e tenacidade à fratura tornando a ferramenta ou peça muito dura e pouco tenaz.pt_BR
dc.description.abstractenThe composite WC-10% Co is one of the materials most produced by the hardmetal fabrication industry. However, a better understanding of the effect of process parameters on their structural characteristics is sought, especially with respect to the formation of metastable phases - η. In this work, we used the Rietveld Method with X - Ray Diffraction (XRD), Scanning Electron Microscopy (SEM) and Brunauer - Emmett - Teller (BET) to investigate the structure of the raw materials used in the production of hardmetal. The particle sizes as well as the identified morphologies for the WC and Co powders are reflections of their manufacturing process, which introduce residual stresses for WC powder, low crystallinity and a significant amorphous portion for Co powder. These characteristics were identified with XRD in comparison to the obtained diffraction pattern and crystallographic databases. After the powder mixing process, the phases were quantified and the effects of this process were identified on the unit cells of each phase. This work shows that the characterization route using the Rietveld Method is efficient to analyze the structure of these materials during their processing. It was observed that the mixing process using high energy milling equipment promotes a change in the density of WC unit cells by “pushing” Co atoms into their structure. This may accelerate the dissolution process of most WC particles during sintering. And contribute to the accentuated formation of metastable phases eta – η, damaging the balance between the mechanical properties of hardness and fracture toughness making the tool or piece very hard and not very tenacious.pt_BR
dc.identifier.citationBATISTA, A. C. et al. Caracterização da matéria-prima com tamanho de partículas nanométricas utilizadas no processamento do compósito WC-10%Co. Matéria, Rio de Janeiro, v. 25, n. 3, artigo e-12813, 2020. Disponível em: <https://www.scielo.br/j/rmat/a/wMPH6vLk5Y3ZKYKkjy98ddw/?lang=pt>. Acesso em: 12 set. 2021.pt_BR
dc.identifier.doihttps://doi.org/10.1590/S1517-707620200003.1113pt_BR
dc.identifier.issn1517-7076
dc.identifier.urihttp://www.repositorio.ufop.br/jspui/handle/123456789/14267
dc.language.isopt_BRpt_BR
dc.rightsabertopt_BR
dc.rights.licenseEste é um artigo publicado em acesso aberto (Open Access) sob a licença Creative Commons Attribution, que permite uso, distribuição e reprodução em qualquer meio, sem restrições desde que o trabalho original seja corretamente citado. Fonte: o PDF do artigo.pt_BR
dc.subjectWC nanométricopt_BR
dc.subjectMetal duropt_BR
dc.subjectDifração de raios Xpt_BR
dc.subjectCaracterização de materiaispt_BR
dc.subjectMétodo Rietveldpt_BR
dc.titleCaracterização da matéria-prima com tamanho de partículas nanométricas utilizadas no processamento do compósito WC-10%Co.pt_BR
dc.title.alternativeCharacterization of the raw material with nanometric particle size used in the processing of the composite WC-10% Co.pt_BR
dc.typeArtigo publicado em periodicopt_BR
Files
Original bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
ARTIGO_CaracterizaçãoMatériaPrima.pdf
Size:
551.77 KB
Format:
Adobe Portable Document Format
Description:
Download
License bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
license.txt
Size:
1.71 KB
Format:
Item-specific license agreed upon to submission
Description:
Download
Collections
DEMET - Artigos publicados em periódicos