Alencar, Lorena Dariane da SilvaMesquita, AlexandreFeitosa, Carlos Alberto CarneiroBalzer, RosanaProbst, Luiz Fernando DiasBatalha, Daniel CarreiraRosmaninho, Marcelo GonçalvesFajardo, Humberto VieiraBernardi, Maria Inês Basso2018-03-132018-03-132017ALENCAR, L.D. da S. et al. Preparation, characterization and catalytic application of Barium molybdate (BaMoO4) and Barium tungstate (BaWO4) in the gas-phase oxidation of toluene. Ceramics International, v. 43, n. 5, p. 4462-4469, abr. 2017. Disponível em: <http://www.sciencedirect.com/science/article/pii/S0272884216323641>. Acesso em: 15 set. 2017. 0272-8842http://www.repositorio.ufop.br/handle/123456789/9612Barium molybdate and Barium tungstate are important materials due their photoluminescent properties and they also have catalysis and photocatalysis applications. In this work, powders of these compounds were prepared by microwave-assisted hydrothermal (MAH) method and polymeric precursor method (PPM) and their structural and optical properties were studied. Furthermore, these materials were employed as solid catalysts towards gas phase toluene oxidation reactions. X-ray diffraction confirms the purity of materials at both preparation methods and reveals a preferential growth when the powders are prepared by MAH due polymeric agents and processing using microwave, which was confirmed by Field emission scanning electron microscopy. Photoluminesce emission was attributed to the charge-transfer transitions within the [WO4]2- and [MoO4]2- complexes. The H2 Temperature-Programmed Reduction (H2-TPR), O2-chemisorption and extended X-ray absorption fine structure (EXAFS) results indicated that BaWO4 samples, compared with BaMoO4 samples, have higher oxygen mobility and oxygen vacancies that appear as key factors for the achievement of better catalytic performances.en-USabertoMicrowave-assisted hydrothermalPolymeric precursorArtigo publicado em periodicoO periódico Ceramics International concede permissão para depósito deste artigo no Repositório Institucional da UFOP. Número da licença: 4210801039274.https://doi.org/10.1016/j.ceramint.2016.12.096